Q345R steel plate
Origin: bbn STEELThickness: 6mm to 350mm
Length: 200mm to 18000mm
Payment terms: L/C, T/T
Commitment: If we have no the size in stock, it takes about 20 days for us to produce the Q345R steel plate for you if the quantity can be more than 10 tons.
Describe:Hot rolled steel strip with JIS standard SPHC - shenda-steel…Hot rolled steel strip with JIS standard SPHC,US $ 310 - 490 / Metric Ton, AISI, ASTM, BS, DIN, GB
Inquiry (Leave message and get the latest price)Q345R steel plate Equivalent
Q345R steel plate
Q345R steel plate is the most used materials to build specified elevated boilers and pressure vessels,with good mechanical properties and process performance, it is China's most widely used, the largest amount of special steel pressure vessel.The best equivalent steel grade with Q345R is A516 Grade 70 in specification ASTM A516/A516M.
Q345R steel contains a certain amount of alloy elements, yield strength tends to be high.
Mechnical Property for Q345R Pressure Vessel Steel:
Thickness (mm) | ||||||
Q345R | > 3 ≤ 16 | > 16 ≤ 36 | > 36 ≤ 60 | >60 ≤ 100 | >100 ≤ 150 | >150 |
Yield strength (≥Mpa) | 345 | 325 | 315 | 305 | 285 | 265 |
Tensile strength (Mpa) | 510-640 | 500-630 | 490-620 | 480-610 | 470-600 |
Chemical Composition for Q345R Pressure Vessel Steel (Heat Analysis Max%)
Main chemical elements composition of Q345R | |||||
C | Si | Mn | P | S | Alt (min.) |
0.20 | 0.55 | 1.20-1.60 | 0.025 | 0.015 | 0.020 |
Q345R is a combination of 16Mng, 19 Mng and GB6654-1996, and GB150 specified the thickness range is 3 ~ 200mm. The limit value of the tensile strength with low carbon content and standard is no more than 540Mpa, and it has good weldability, in common conditions cold and hot crack are not easy to form. However, the same as the 20 # carbon manganese structure steel, with large thickness and in low ambient temperature working environment, it produces cold, hot cracks.
If you want to know more about Q345R Pressure Vessel Steel Plate,please contact us,we will give you the best service.